Stoody NiCrMo3-T1
Stoody NiCrMo3-T1 is a gas shielded flux cored wire that can be used for welding in all positions using argon/CO2 mixtures. The wire possesses excellent weldability and can be used in a wide variety of similar and dissimilar welding and cladding applications. The iron content of the all-weld deposit is kept below 1% for applications requiring enhanced corrosion resistance.
Features
- Joining nickel-chromium-molybdenum alloys to UNS N06625. Clad side of joints in steel clad with nickel-chromium-molybdenum weld metal Surfacing steel with nickel-chromium-molybdenum weld metal Joining steels to nickel based alloys Joining 9% nickel steel for cryogenic applications
Industries
- Petrochemical
Typical Charpy V-Notch Properties
| as welded asme testing using 1 in. thick 9% ni, 3g | ||||
| as welded | ||||
Typical Tensile Properties
| Condition | As Welded | As Welded |
| ASME Testing Using 1 in. Thick 9% Ni, 3G, Cross-Joint | ||
| Tensile Strength | 725 MPa (105 ksi) | 714 MPa (104 ksi) |
| Yield Strength | 470 MPa (68 ksi) | |
| Elongation | 38 % | |
Recommended Welding Parameters
| Current | 150-200 A |
| Shielding Gas | 75% - Ar/25% - CO2 |
| Voltage | 25-27 V |
| Wire Diameter | .045 in. |
| Wire Diameter | 1.2 mm |
| Wire Feed Speed | 290-400 in./min |
| Wire Feed Speed | 735-1000 mm/min |
Classifications
| Classifications |
ISO : TNi 6625-14 ENiCrMo3T1-4 : AWS A5.34/A5.34M : 2018 |
Typical Weld Metal Analysis %
| Typical Weld Metal Analysis % | ||||||||||||||
| C | Co | Cr | Fe | Mn | Mo | Nb+Ta | Ni | P | S | Si | Ti | |||
| 0.02 % | 0.02 % | 21.0 % | 0.3 % | 0.2 % | 8.5 % | 3.3 % | Balance % | 0.005 % | 0.003 % | 0.35 % | 0.1 % | |||
Part Numbers and Accessories